What is brick of heat preservation of white of light qualitative Mo Laishi? It is to choose tall purity fireproof insulation material, set scale by handicraft, add organic chemistry compound model stuff stuff, via vavuum pump extruding is machined, the handicraft of light qualitative Mo Laishi that tall to calcine generates.
Brick of heat preservation of white of light qualitative Mo Laishi
Brick of heat preservation of white of light qualitative Mo Laishi
Tall Mo Laishi pledges adiabatic brick is the new technology application that introduces in our country, the environmental protection of Chinese new fund is energy-saving and fireproof insulation material, have heat-resisting. Compressive strength tall diathermancy can be good, environmental protection is energy-saving effect is distinct wait for character, crude oil of in order to cracks interpose furnace. Metallurgical industry hot-blast stove, kiln of china roller path, channel kiln, electric porcelain cabinet, kiln of boiler of sandwich glass clamp reachs li of line of various heating furnace, but instantly flame of lay a finger on. Show level to apply via relevant enterprise, this commodity achieves the various function target of foreign congener commodity. High quality kiln furnace Wu should use new raw material, strange raw material in other words is tall Mo Laishi is qualitative adiabatic and fireproof insulation material.
Characteristic: Pure degree tall, sludge content is little, heat-resisting, but instantly flame of lay a finger on, be able to bear or endure corrode of various atmosphere dip, low conduct heat, low hot be in harmony, tall tenacity, and have high accuracy of high quality norms of heat-resisting shake character, but optional laser cut.
Pledge gently with its and the character with good character of adiabatic heat preservation, the line of hot side fire prevention that Mo Laishi pledges market of heat preservation brick applies at equipment of varied adiabatic machine gently or thermal insulation, produce specialty to promote the power energy resources of machine equipment utilization rate, with not coming the tall aluminium of Shi Zhujing photograph makes fireproof insulation material, water content of general ferric oxide is among 65%-75% . of fire prevention of light qualitative brick spends Mo Laishi can accomplish 1790 ℃ to control. Load molten just began to spend 1600-1700 ℃ . Experiment of the compression below normal temperature is slight 70-260MPa. Heat-resisting shake sex is admirable. Have to calcine Mo Laishi brick and Mo Laishi of electric frit pipe fitting brick 2 kinds.
To calcine pledges brick of heat preservation of Mo Laishi white is crucial raw material with grog of cement of tall aluminous alumina gently, add grain clay or give birth to the aluminous mixture that make fuse, via figuration, fire make it. Electric frit pipe fitting not comes stone brick is raw material with ferric oxide of tall aluminous alumina, manufacturing industry and fireproof clay, add wooden carbon or anxious carbon grit to do oxidizer, choose after figuration recover from an illness a future life of law of electric frit pipe fitting is produced go to.
The knot crystal of electric frit Mo Laishi is bigger than to calcine Mo Laishi, heat-resisting shake performance is better than to calcine handicraft. The water content that their tall characteristic key depends on ferric oxide and the well-balanced sex that sandwich glass of get along with spreads all over Molaishi. Mo Laishi pledges adiabatic brick is to be in our country new-style fireproof insulation material, but instantly flame of lay a finger on, have heat-resisting, slight tall, conduct heat coefficient small, environmental protection is energy-saving effect is distinct wait for character. Li of line of boiler of clamp of kiln of cabinet of porcelain of kiln of path of roller of furnace of applicable splitting decomposition, hot-blast stove, china, report, sandwich glass and various heating furnace.
Choose show level to pledge production of brick of Mo Laishi heat preservation makes common grouting shape gently law, nature maintains to after giving a model, move into forced impetuous works in air desiccator, all previous classics is subsequently tall fire, all previous of fire base substrate produces treatment via polish of mechanical equipment burnish is finished products namely.
Is makings order cast to be: in blending whole process? ? of herd of  of Jiao of late of the Yong that bear press and smooth is blended well-balanced hind, add wood chip pink to be blended again well-balanced, add water subsequently. The accretion of water is measured operate commonly in 50% fluctuation, make expect the oar maintains pretty good negotiability, be helpful for figuration, additional, so that water portion is overmuch, the harm maintains between .
In the whole process that blends mix up, also want to add the agent decreasing water such as intensifier of additive, green compact to wait. Wait for pug mix up to become silty later, add antiseptic A, once more mix up is well-balanced. What will made is silty the figuration in introducing hypostatic model, indoors below temperature static put maintain, make silty in the water share that does not want is changed dispersedly and volatilize, general static put 24h to be able to give a model up and down, at this moment the water portion of slimy base is in 35% fluctuation. Fall when water portion when 25%~30% , impetuous car works to enter air desiccator to begin on base substrate mandatory dry impetuous, dry impetuous is spent after can accomplishing 110 ℃ ; to do impetuous 24~48h more, be less than when portion of base substrate water 2% when, go up kiln fire.
Fire is begun in the kiln of type of natural gas shuttle of 20m3, fire spends 1300 ℃ , 4h of adiabatic heat preservation, heat falls to leave listed pit to 200 ℃ after armistice, the wool embryo all previous after fire is machined via deepness of polish of mechanical equipment burnish, after amounting to mark, detecting is finished products namely. Commodity exterior is white, those who give air hole to see 1mm fluctuates more is small give air hole. As comparative as the commodity exterior that is the agent that make hole with ball of EPS grain content, give air hole smaller more well-balanced, colour and lustre is more meticulous.
Independence application wood chip as the agent that make hole, choose form a vesicle to shape law, add the antiseptic of certain amount, can produce make the Molaishi with a high quality character brick of light qualitative heat preservation. This treatment craft is simple and easy, appropriate big batch is produced, and do not use EPS raw material, save cost to expend already environmental protection. Production makes brick of yield heat preservation of white of light qualitative Mo Laishi be 0.57g · Cm-3 to fluctuate relative to density, 400 ℃ conduct heat coefficient is 0.16W · (M · K)-1, commodity conducts heat coefficient index value is good at extensive commodity, energy-saving and practical effect enhances environmental protection in the round, have first-rate economic gains and socioeconomy beneficial result.