The manufacturing technology of magnesian chromic brick

March 15, 2024Nov 23, 2024

The manufacturing technology of fire magnesium chromic brick and general similar. Be in to eliminate a brick firing the as a result of MgO and CrO, AlO or iron oxide reaction in the process is generated

Pointed spar

The expand and causes inattentive effect when, also can use compound collective

Agglomeration makings

Make magnesian chromic brick. In addition, still have do not burn magnesian chromic brick, for example, do not burn magnesian chromic brick with what solution of inorganic magnesium salt is united in wedlock.




Do not burn magnesian chromic brick to manufacture technology simple, cost is low,

Thermal stability

It may not be a bad idea, but high temperature intensity is far not as good as firing brick. 50 time end, development goes a kind of alleged “ to combine ” magnesium chromic brick directly. The characteristic of this kind of brick is raw material pure, firing temperature is high,

Square magnesian stone

,

Pointed spar

Etc be united in wedlock directly between high temperature photograph, the low frit photograph such as silicate distributings for Gu island shape, accordingly, the high temperature strength that increased a brick significantly and the sex that fight broken bits.



The mine that use chromium - the fine noodles or vermicelli made from bean or sweet potato starch that after magnesia grinds the to calcine that control base in all, makes, with magnesia thick grain cooperates to formulate bricky method, it is the significant step that removes inattentive effect the magnesian chromium brick that becomes with this kind of honest legal system, with common magnesium chromic brick photograph is compared, bricky porosity is low,

Loading bate temperature

And

Fight lose strength

All taller. The mine that use chromium - magnesite pink controls base, the synthetic magnesian chromium of to calcine of classics high temperature is arenaceous the magnesian chromic brick that makes,



Magnesian chromium of melt of furnace of Gu of useful still report expects direct casting and gotten founding magnesium is chromic brick

, the frit bead recombine that with electric frit magnesium chromic makings presses the craft that make a brick to produce is magnesian chromic brick.