Silica ramming mass is made of quartz (SiO2) refractory raw material as aggregate and a certain proportion of powder, binders and additives.
Service Temperature: 1600-1700℃
SiO Composition Proportion: 90%
Bending Time: 1-2h/2-3h

Alumina ramming mass is an amorphous refractory made from bauxite clinker as aggregate, powder. It is constructed with manual or mechanical ramming and then heated to form an inner lining to resist slag erosion.

Characters
High density
Good flexibility
Good chemical stability
Good thermal stability

MgO:78-82%
For magnesium brick

SiO2:≥92%
For silica brick

Al2O3%:48-65%
For high alumina brick

Al2O3: 42-80%
For fire clay bricks

Material: Calcium aluminate
Paper bags: 25/50kg
Big bags: 1.0/1.5mt