Fight flake tall aluminous brick

Fight flake tall aluminous brick, according to its name we can be clear about a medium kind to it is product of tall aluminous brick. Fight flake tall aluminous brick is with fancy tall aluminous alumina clinker and the synthetic material that contain Zr02 are raw material, according to what deserve certainly to be made than shaping via high pressure firing goods. We let understand this kind of fireproof product below.
Fight flake of tall aluminous brick fight flake capability is strong, have at the same time fight potassium, natrium, sulfur, chloric reach alkalescent salt erode, the function such as low thermal conductance, it is cement kiln transfers belt and the good material that distribute ungird, the marked characteristic of goods is heat-resisting shake function good, acclimatization capability is strong. Multi-purpose be taken at revolving warm-up or decompose the place such as cold machine of comb with a double-edged fine-toothed comb is reached inside furnace.


We flake according to fighting the manufacturing technology of tall aluminous brick and raw material deserve to be like next performance advantages than discovering it:
1, reduce canister temperature to spend 50 ℃ above, make sure hot-working equipment safety moves, reduce red kiln phenomenon;
2, raise rotary kiln to heat up use efficiency, reduce the sources of energy to use up 5% above, improve enterprise beneficial result;
3, integral performance is good, use volume effectively bigger than composite products, fight wear away cycle is long;
4, wear away when goods 1/2 when, composite products will not be used, and fight flake tall aluminous brick can insist to use the rest 1/3 place.
Fight flake manage of tall aluminous brick changes target:


Fight a kind of when flake tall aluminous brick is our country original creation new-style and fireproof material, reach advanced level. This kind of brick has superior natural science to change target: Thermal shock stability falls in 1000 degrees ＞ 40, fireproof degree it is 1780 degrees, it is 1470 ℃ ～ with heavy bate temperature 1520 ℃ , heat expands rate is low, coefficient of thermal conductivity is small, fight grind anti-corrosive, can replace large and new-style dry method kiln is firing the fireproof material of all place beyond the belt.
Fight flake tall aluminous brick compares tall aluminous brick and tradition. Thermal shock stability is outstanding, intensity is high, fight chemistry to corrode, hot coefficient of expansion is small, coefficient of thermal conductivity is low, firing temperature is low, comprehensive ground improved material function, dropped greatly specific power consumption.
Fight flake tall aluminous brick has following characteristics: Temperature of bate of excellent thermal shock stability, loading it is certain that tall, alkali resistance and grog erode intensity of tall, high temperature wear-resisting of mechanical intensity, high temperature, fight flake, low, service life grows group of the skin that fight a form, cement and coefficient of thermal conductivity wait for composite characteristic.


Fight flake the brick applies tall aluminium successfully to concern place at cement kiln, use at regenerator of kiln of glass of large surplus law, replace traditional magnesian chromic brick, lengthened kiln furnace to use life not merely, and eliminated chromic social effects of pollution. In addition, fight fall off of tall aluminous brick firing temperature should compare magnesian chromic brick low about 300 ℃ , energy-saving action is quite sizable.
Accordingly, we wait for kiln furnace domain to be able to advance logical choice to fight according to the project in rotary kiln flake tall aluminous brick, reduce specific power consumption to improve kiln furnace performance.