Does tall aluminium get together can light brick replace Molaishi to get together light brick?

March 15, 2024Nov 25, 2024


Tall aluminium gets together light brick and Molaishi get together light brick is a kind of light qualitative fireproof heat-insulating material, use at the adiabatic heat preservation in furnace of high temperature kiln normally. Although their in some way has similar character, but also put in a few difference.
Mo Laishi gets together light brick is the heat preservation brick that with Molaishi brilliant photograph gives priority to, and tall aluminium gets together light brick basically is raw material with tall aluminous mine. Both material composition is different, because this is on function may somewhat difference.
Tall aluminium gets together light brick is main raw material with aluminous alumina, complementary use with proper additive get together to burn the production that break a law gently. Goods has strength tall, thermal stability is good, the heavy change that burn fine is little, coefficient of thermal conductivity is small wait for a characteristic. Get together price of light tall aluminous brick is in more than 2000 reach three tons, also differ according to the difference price of aluminous content, this is market reference price, particular value needs to produce the decision after manufacturer talks things over with firebrick. Get together light tall aluminous brick is fireproof temperature is high, alumina content is in 48% above, specific gravity 0.4-1.35g/cm3, porosity 66% ~ 73% , compression intensity 1 ~ 8MPa. The light qualitative fireproof material that basically constitutes jointly by Molaishi and vitreous photograph or corundum. Heatproof shake performance is better.
Tall aluminium gets together light brick has higher compressive strength and fireproof property normally, the adiabatic and adiabatic heat preservation that applies to environment of a few high temperature to fall, and erode without stock of melt of intense high temperature reach erode the place of action. When be being contacted with blaze directly, temperature of watch surface contact does not get prep above 1350 ℃ .


Mo Laishi gets together light brick has its advantage in temperature respect, use temperature gets together than tall aluminium light brick wants tall, but the price slightly expensive. Density of this product volume is in commonly 0.6-1.2g/cm3, use temperature 1300 degrees - 1550 degrees. Different dimension can pursue order do. According to use temperature cent is JM-23, JM-26, JM-28, JM30, a few kinds of model such as JM32, this kind of product can contact blaze directly, have spend tall, coefficient of thermal conductivity high temperature resistantly, gently small, energy-saving wait for a characteristic.
Does tall aluminium get together can light brick replace Molaishi to get together light brick? Whether can replace should depend on specific applied setting and demand. Good method is to undertake detailed comparison is mixed evaluate, in order to decide which kinds of material fits your specific project more.
Get in Touch
Fill out the short form below and we will be in touch.
linkedin facebook pinterest youtube rss twitter instagram facebook-blank rss-blank linkedin-blank pinterest youtube twitter instagram question-circle